At present, many industries need to use different specifications and sizes of C steel, so they need to carry out fine cutting of C steel. At this time, some CNC machines can complete the cutting of CNC steel plates. When using the equipment, be sure to do a good job to ensure the cutting effect. Now let's talk about the correct operation of CNC cutting of Jinan C beam.
Attention should be paid to some details when finishing the CNC cutting of C-beam, especially the cutting speed should not be too fast. If you only pursue cutting speed, you will ignore many details, which easily leads to the consumption of some waste and raw materials. Therefore, it should be noted that the cutting speed should not be too fast, and the cutting speed should be as low as possible to improve production efficiency.
Secondly, do a good job of preheating. As we want to conduct CNC cutting of C-beam, we need to preheat it first. Some steel plates are easy to produce cracks during cutting, and some are caused by low temperature. Therefore, we should pay attention to preheating. First, preheat the steel plate to gradually increase its temperature, and then cut it to ensure the processing quality of C-shaped steel.
But when cutting, we should pay attention to many aspects, including details, preheating, etc. These should be noted. Only in this way can we ensure that the cutting is completed and the required beam is obtained.
In addition, we will carefully check whether there are any problems in receiving the goods after our C-beam manufacturer delivers the goods. Everyone should have no problem with this. Secondly, if there are many types of section steels purchased later, it is recommended that they be stacked separately when they are stored to avoid the damage of C-section steels and facilitate the handling and management.
Then, the C-shaped steel shall be stored stably, and the stacking height shall not be too high, so as to avoid the danger of profile slipping. In addition, the warehouse of C-shaped steel shall be clean, dry and ventilated, and no corrosive materials such as acid, alkali, salt and cement shall be placed in the warehouse.
It is necessary to clarify the specific thickness and delivery status of steel plate, including forging and rolling. Forging is very rough, with low density and low price. Therefore, in general, it is necessary to explicitly inquire about and select the delivery status of rolling solution. The suggestion that the price is too low is prudent. More relevant content will come to our website http://www.jnhscg.com consulting service